• Modell Nr.: 3.2mm
• Form : Wohnung
• Aussehen : Flachtemperierte
• Standard : GB15763.2-2005
• Stahl Degree : Super-gehärtetes Glas
• Fragment Staat : Ⅲ
• Technics : Körperlich Temperierte
• Ebenheit : High Class

• Trademark: Huamei
• Packing: Wood Cases with Paper Interlayer
• Standard: ISO, CE, SPF
• Origin: Jiangsu, China
• HS Code: 70071900
• Production Capacity: 8000000 Sqm Per Year

High Quality 3.2mm Toughened Solar Glass for Solar Cell,combined with nanometer anti-reflective coating Low Iron Solar PV Glass with Low Reflectanceay of decreasing light reflectance and improve the solar  cell phtotelectric conversion efficiency.Meanwhile,it reduces the reflected glare of the glass and the pollution caused by the reflectance to the environment. The hydrophobic behavior of the AR coating could in some degree protect the dust and dirt from shading the light and improve the cleaning performance of the glass. With the outstanding characteristics of the high solar lights transmittance, the low reflectance, the low iron, the high mechanical strenght and the high flatness, it is one of the indispensable important parts of solar cell and has been widely used to photovoltaic power generation all over the world.

Products	High Quality 3.2mm Toughened Solar Glass for Solar Cell
Thickness	3.2mm,4.0mm
Size	Can be customized,maximum size:1200*2200mm
Solar transmittance	3.2mm>93.6%,with AR coating
Applications	For solar cell module
Payment terms	T/T
Delivery	Within 15 days after receiving the deposit
MOQ	20‘FCL
Port	Shanghai

Features :
1.     High solar lights transmittance
2.     The low reflectance: visible light reflectance is less than 7.30%
3.     Low iron:glass has only 0.012% of iron content;
4.     High intensity,the strength is 3-5 times of ordinary annealed glass
5.     Wind pressure resistance: the wind pressure resistance is 1.5-3 times of ordinary annealed glass;
6.     Heat shock resistance: the heat shock resistance is 3 times of ordinary annealed glass;
7.     Safety:if it is broken, it usually breaks into relatively small pieces, which are less likely to cause serious injury.

	Test	Standards	Test method	Results
1	Appearance	EN1096-2	Surface is clean, no scratches,spots or pinhole	Qualified
2	Light transmittance	ISO 9050	The ratio after coating is higher than before >2.5	>2.6
3	Adhesion	ASTMD3359	The cutting edge is very smooth , no grid slide,	0 level
4	Pencil hardness	ASTMD3363	No thickness of film which scratched by pencil more than 3mm	≥6H
5	Salt spray test	EN1096-2	With 5%(±1)NaC1,under 35ºC,last 4-9days,record  the data before and after the test, T<1.0	4 days,      T=0.57   9 days,      T=0.91
6	Thermal Cycle	IEC61215/10	Keep the temperature between -40ºC and 85ºC,±2ºC,200 times,(around 1000 hours),record  the data before and after the test,T<1.0	T=0.48
7	Muggle Test	IEC61215/10	Under 85ºC,±2ºC,relative humidity is 85ºC,±5ºC,around 1000 hours,record  the data before and after the test,T<1.0	T=0.63
8	Wet-cold test	IEC61215/10	Humidity is 85,±5ºC,temperature is 85ºC,±2ºC,fall to -40ºC,cycle for 10 times.Record  the data before and after the test,T<1.0	T=0.80
9	Outdoor exposure	IEC61215/10	Test with the moniter in outdoor temperature,total radiation need to be 60kmh·m-2 .Record  the data before and after the test,T<1.0	T=0.59
10	Mechanical Loading	IEC61215/10	Adding the load to 2400Pa and make it distributed.Keep 2-3 times;the layer wasn't broken and no serious defects in appearance	Qualified

Production process:
Raw material——>Edging and cleaning——>In-process inspection——>Coating——>Tempering——>Cleaning——>Packing

Packing:
1. Interlay paper between two sheets. 
2. Seaworthy wooden crates. 
3. Plastic belt for consolidation.

Our service: 
1.Reply your inquiry in 24 working hours.
 2.Customized design is avaliable ,OEM is welcome .
 3.Delivery the goods to our customer all over the world with speed and precision.
 4.Offer customer the products with good quality and competitive price.
 

» » »